PP--Nanjing Hongrui Plastic Products Co., Ltd.

Item	Test Standard	Unit	Typical Performance
Item	Test Standard	Unit	P1000	P1304	P201	P401	P302	P304	P306	P3010	P830	P840	P860	P353
Density	D792	g/cm³	1.15	1.28	0.90	0.90	1.02	1.08	1.14	1.34	1.00	1.04	1.14	1.42
Tensile Strength	D638	MPa	20	30	15	20	30	60	80	90	20	25	30	120
Elongation at Break	D638	%	2	2	100	10	2	2	2	2	3	3	3	2
Bending Strength	D790	MPa	30	60	20	25	50	80	100	120	30	35	45	190
Flexural Modulus	D790	MPa	1200	2800	800	1000	2500	3500	4500	6000	1200	1500	2000	7500
Notched Impact Strength of Cantilever	D256	kJ/㎡	5.0	5.0	40.0	15.0	6.0	7.0	7.0	6.0	5.0	6.0	6.0	5.0
Rockwell Hardness, HRR	D785	——	90	100	60	70	110	110	115	118	90	100	105	120
Melting Point		℃	170	175	170	170	175	175	175	175	170	170	170	175
Heat Distortion Temperature, 0.45MPa	D648	℃	90	140	85	90	120	130	145	150	100	110	120	140
Flame Retardance	UL94	Grade	V0	V0	HB	HB	HB	HB	HB	HB	HB	HB	HB	HB
Surface Resistance	D257	Ω	10¹⁵	10¹⁶	10¹⁶	10¹⁶	10¹⁶	10¹⁶	10¹⁶	10¹⁶	10¹⁴	10¹⁴	10¹⁴	10¹⁵
Dielectric Strength	D149	KV/mm	19	19	15	15	15	15	15	15	19	19	19	16
Mould Shrinkage	D955	mm/mm	0.01	0.004	0.02	0.018	0.008	0.005	0.003	0.002	0.016	0.015	0.01	0.001
Filling Amount		%	——	GF20	——	——	GF10	GF10	GF30	GF50	M15	M20	M30	GF15+M25
Features			General flame retardant type	Glass fiber reinforced flame retardant type	Toughening high impact type		Glass fiber reinforced type				Mineral reinforced type			Glass fiber mineral reinforced type
Use			Electronic component	Electronics connector	Automotive radiator		Textile equipment, engine blower, auto parts, electronic components				Auto parts, electronics, mechanical parts			Mechanical parts